The following typical properties are not guaranteed since in most cases they are averages for various size, product forms and methods of manufacture and may not br exactly representative of any particular product or size. This data is intended only as a basis for comparing alloys and tempers and shoud not be specified as engineering requirements or used for design prposes.
Typical Mechanical Properties * (1)
| TENSION |
HARDNESS |
SHEAR |
FATIGUE |
MODULUS |
| Alloy and Temper |
HStrength ksi |
Elongation percent in 2 |
Brinell Number
500 kg load 10mm ball |
Ultimate Shearing Strength
ksi |
Endurance(2) Limit
ksi |
Modulus(3) Of Elasticity
ksi x 103 |
| Ultimate |
Yield |
1/16 Thick Specimen |
1/2 Diameter Specimen |
| 2011-T3 |
55 |
43 |
- |
15 |
95 |
32 |
18 |
10.2 |
| 2011-T8 |
59 |
45 |
- |
12 |
100 |
35 |
18 |
10.2 |
| 2014-O |
27 |
14 |
- |
18 |
45 |
18 |
13 |
10.6 |
| 2014-T4, T451 |
62 |
42 |
- |
20 |
105 |
38 |
20 |
10.6 |
| 2014-T6, T651 |
70 |
60 |
- |
13 |
135 |
42 |
18 |
10.5 |
| 2017-O |
26 |
10 |
- |
22 |
45 |
18 |
13 |
10.5 |
| 2017-H13 |
35 |
33 |
- |
10 |
- |
- |
- |
10.5 |
| 2017-T4, T451 |
62 |
40 |
- |
22 |
105 |
38 |
18 |
10.5 |
| 2024-O |
27 |
11 |
20 |
22 |
47 |
18 |
13 |
10.6 |
| 2024-H13 |
37 |
35 |
- |
9 |
- |
- |
- |
10.6 |
| 2024-T351, T4 |
68 |
47 |
20 |
19 |
120 |
41 |
20 |
10.6 |
| 2024-T361 |
72 |
57 |
13 |
- |
130 |
42 |
18 |
10.6 |
| 2024-T851 |
70 |
65 |
6 |
- |
128 |
43 |
18 |
10.6 |
| 6061-O |
18 |
8 |
25 |
30 |
30 |
12 |
9 |
10.0 |
| 6061-H13 |
26 |
- |
- |
- |
- |
- |
- |
10.0 |
| 6061-T4, T451 |
35 |
21 |
22 |
25 |
65 |
24 |
14 |
10.0 |
| 6061-T6, T651 |
45 |
40 |
12 |
17 |
95 |
30 |
14 |
10.0 |
| 6061-T913 |
67 |
66 |
- |
10 |
- |
35 |
- |
10.0 |
| 6061-T94 |
57 |
- |
- |
- |
- |
- |
- |
10.0 |
| 6063-O |
13 |
7 |
- |
- |
25 |
10 |
8 |
10.0 |
| 6063-T4 |
25 |
13 |
22 |
- |
- |
16 |
- |
10.0 |
| 6063-T6 |
35 |
31 |
12 |
- |
73 |
22 |
10 |
10.0 |
| 6262-T6, T651 |
45 |
40 |
- |
17 |
95 |
30 |
- |
10.0 |
| 6262-T9 |
58 |
55 |
- |
10 |
120 |
35 |
13 |
10.0 |
| 7075-O |
33 |
15 |
17 |
16 |
60 |
22 |
17 |
10.4 |
| 7075-H13 |
40 |
- |
- |
- |
- |
- |
- |
10.4 |
| 7075-T6, T651 |
83 |
73 |
11 |
11 |
150 |
48 |
23 |
10.4 |
| 7075-T73,T7351 |
73 |
63 |
13 |
- |
- |
44 |
23 |
10.4 |
Notes:
(1)- the indicated typical mechanical properties for all except 0 temper material are highter than the specified minimum properties. For O temper products typical ultimate and yield values are slightly lower than specified (maximum) values.
(2) - Based on 500,000,000 cycles of completely reversed stress using the R.R. Moore type of machine and specimen.
(3) - Average of tension and compression moduli. Compression modulus is 2% greater than tension modulus.
|